Report 4890022 from French Testing Laboratory

Smoke Emissions & Toxicity to NF F-16-101 & 102

Result F0

Report 64100 Warrington Fire Research

Spread of Flame to NF F 92-501

Result M1

Report L14066 Warrington Fire Research

Optical Density of Smoke Solid Materials ASTM E662-83

Flaming Mode: 99.42 Non Flaming: 198.38

Report L14680 Warrington Fire Research

Test for Fire Propagation of Building Materials, to BS 476 Pt.6 Class 0

Report L14534 Warrington Fire Research

Surface Spread of Flame to BS 476 Pt.7

Class 1

Report L14535 Warrington Fire Research

3m³ Smoke Emission Test to BS 6853

Ao (max) 138.23 (Category 1)

Report L14536 Warrington Fire Research

Analysis of Pyrolysis and Combustion Gases to N FX 70-100

R value 0.28

Report L14537 Warrington Fire Research

Cone Calorimeter Test to ISO 5660

Average HRR 48.9 KW/m²

Report Schaemen T 5701.1

Fire Resistance to DIN 54837 and DIN 5510-S-4 UIC Test

Class A

Report Satra Tech. Services No.16480/9609/2/B/D/MG/MD

Slip Resistance of a smooth finish flooring to London Underground specification

- PASS

Report TE 88065/6 form LUL Technology Services

Composite Flooring Tested to BS 476 Pt. 6 (1989) and BS 476 Pt. 7 (1987)

– Class 0

Heat Release Rate (Calculated)

8.18 MJ/kg (41.3MJ/m³ for 3mm material)

Report C10414 from LUL Technical Services

Smoke Emission & Toxic Fume Emission tested as composite – meets LUL " Code of Practice for Fire Safety of Material used in the Underground"

Report 6120015 – DMAT/1 from Laboratoire National d'Essais

Fire Resistance

Result M1

Report F104206 Danish Institute Fire Technology

UIC Kodex 564-2 App. 12

Class 2

Report 27209/6/97 from Wira Testing Centre

Critical Radial Flux of Floor coverings to ANSI/ASTM E648 96a/NFPA 253 1995

Result Category 1

PHYSICAL PROPERTIES  TM7

PROPERTY

TEST METHOD

RESULT

Hardness IRHD

BS 903 Pt. A6

87° to 97^o

Density g/cm³

BS 903 Pt. A1

1.7 ± 0.08gsm/cm²

Tensile Strength kg

ASTM F152 'C'

>45 kg/cm²

Abrasion Resistance H22 Wheels 500 gm wt

3000 Cycles

70% Vacuum

Teledyne Taber Abrader

Weight Loss 1.5 gms

Thickness loss <0.4 mm

Flexibility

>3d

Skid Resistance

RRL Pendulum method 500gm weights

Dry 65 min Wet 18 min

Residual Indentation

BS 810

<1.5%